SERIE 8000 PERFLUOROELASTOMERS

Original Phisical Properties Method Unit Speciment 8010 8012 8014 8025 8030 8034 8045 8048 8050 8058 8070 8090
Color Black White Black Black White White Black White Black Black Black Black
Max Temperatures (range air) °C 260 250 250 260 260 260 300 310 320 320 250 250
Hardness DIN 53505 Sh A 6 mm 75 75 75 75 75 75 75 75 75 90 75 89
Modulus 100% DIN 53504 n/mm2 S2 ≥ 10 ≥ 4 ≥ 8 ≥ 8 ≥ 8 ≥ 4 ≥6 ≥5 ≥5 ≥7 ≥4.3 ≥10.3
Tensile Strength DIN 53504 n/mm2 S2 ≥ 18 ≥ 18 ≥ 14 ≥ 15 ≥ 15 ≥ 16 ≥ 13 ≥ 14 ≥ 12 ≥ 14 ≥ 16.7 ≥ 12.5
Elongation at Break DIN 53504 % S2 ≥ 140 ≥ 110 ≥ 130 ≥ 130 ≥ 130 ≥ 120 ≥ 160 ≥ 180 ≥ 150 ≥ 100 ≥ 257 ≥ 120
72 h 200° C (392°F) DIN 53517 % ≤ 25 ≤ 25 ≤ 20 ≤ 30 ≤ 30 ≤ 25 ≤ 25 ≤ 22 ≤ 30 ≤ 30
72 h 230° C (446°F) DIN 53517 % ≤ 30
72 h 250° C (482°F) DIN 53517 % ≤ 25 ≤ 35
72 h 300° C (572°F) DIN 53517 % ≤ 55
72 h 315° C (599°F) DIN 53517 % ≤ 40
72 h 316° C (600,8°F) DIN 53517 %



SERIE 9000 PERFLUOROELASTOMERS

Original Phisical Properties Method Unit Speciment 9010 9020
Color Translucent Translucent
Max Temperatures (range air) °C 300 300
Hardness DIN 53505 Sh A 6 mm 65 80
Modulus 100% DIN 53504 n/mm2 S2 ≥3 ≥4
Tensile Strength DIN 53504 n/mm2 S2 ≥ 16 ≥ 17
Elongation at Break DIN 53504 % S2 ≥ 250 ≥ 220
72 h 200° C (392°F) DIN 53517 % ≤ 25 ≤ 35
72 h 230° C (446°F) DIN 53517 %
72 h 250° C (482°F) DIN 53517 %
72 h 300° C (572°F) DIN 53517 %
72 h 315° C (599°F) DIN 53517 %
72 h 316° C (600,8°F) DIN 53517 %